RBC-3610 epoxy resin is a thixotropic version of RBC-3600 epoxy resin/epoxy potting compound. It offers the same physical and electrical properties obtained with RBC-3600 epoxy resin. It is especially useful in the aerospace and automotive industries where increased emphasis is placed on high performance from light weight components.
Mixed Viscosity @ 25oC, cps: Thixotropic
Shelf Life, (closed Container @ 25oC): 12 months
Color: Black
Specific Gravity @ 25oC: 0.80
Hardness, Shore D: 80
Linear Shrinkage, in./in.: 0.004
Moisture Absorption 10 Days @ 25oC, %: 0.21
Izod Impact Strength, ft. lbs./in. of notch: 0.24
Tensile Strength @ 25oC, psi: 3,800
Compressive Strength @ 25oC, psi: 11,000
Thermal Conductivity, cal/sec/cm2/oC/cm X 10-4: 3.5
Thermal Stability, 1000 Hrs. @ 175oC, % Wt. Loss: 0.50
Coefficient of Thermal Expansion, in./in./oC X 10-6: 40
Heat Distortion Temperature, oC: 130
Operating Temperature Range, oC: -55 to 140
Volume Resistivity @ 25oC, ohm-cm: 7×1015
Dielectric Strength, volts/mil: 450
Dielectric Constant @ 25oC, 100 KC: 2.80
Dissipation Factor @ 25oC, 100 KC: 0.004
(Note: The above properties are typical of a system cured with hardener #AB-312.)
A-110: A rigid, room temperature curing system with limited pot life and fast cure.
A-120: A resilient, low viscosity system with slightly longer pot life, that exhibits excellent resistance to thermal shock.
AB-312: Good resistance to heat, chemicals, thermal and mechanical shock, and good electrical properties at high humidity.
Weigh the desired amount of #3600 Resin into a clean container and combine with recommended hardener in one of the ratios shown below.
Hardener | Parts by Weight per 100 pts. Resin |
Pot Life 100 grams @ 25oC |
A-110 | 11.2 | 45-50 minutes |
A-120 | 24 | 60-65 minutes |
AB-312 | 26 | 3-4 hours |
Hardener | Cure @ 25oC | Cure @ 65oC | Cure @ 100oC | Cure @ 130oC |
A-110 | 24 hours | 2 hours | — | — |
A-120 | 24 hours | 2 hours | — | — |
AB-312 | — | 6 hours | 3 hours | 2 hours |