RBC-3600 is a low-viscosity, low density, filled epoxy potting resin (epoxy potting compound) used where lightweight castings are necessary without the loss of acceptable physical and electrical properties. RBC-3600 possesses excellent air release and good flowability producing void-free castings. It is especially useful in the aerospace and automotive industries where increased emphasis is placed on high performance from lightweight components.
Mixed Viscosity @ 25oC, cps: 1,300
Shelf Life, (closed Container @ 25oC): 12 months
Specific Gravity @ 25oC: 0.80
Hardness, Shore D: 80
Linear Shrinkage, in./in.: 0.004
Moisture Absorption 10 Days @ 25oC, %: 0.21
Izod Impact Strength, ft. lbs./in. of notch: 0.24
Tensile Strength @ 25oC, psi: 3,800
Compressive Strength @ 25oC, psi: 11,000
Thermal Conductivity, cal/sec/cm2/oC/cm X 10-4: 3.5
Thermal Stability, 1000 Hrs. @ 175oC, % Wt. Loss: 0.50
Coefficient of Thermal Expansion, in./in./oC X 10-6: 40
Heat Distortion Temperature, oC: 130
Operating Temperature Range, oC: -55 to 140
Volume Resistivity @ 25oC, ohm-cm: 7x1015
Dielectric Strength, volts/mil: 450
Dielectric Constant @ 25oC, 100 KC: 2.80
Dissipation Factor @ 25oC, 100 KC: 0.004
(Note: The above properties are typical of a system cured with hardener #AB-312.)
A-110: A rigid, room temperature curing system with limited pot life and fast cure.
A-120: A resilient, low viscosity system with slightly longer pot life, that exhibits excellent resistance to thermal shock.
AB-312: Good resistance to heat, chemicals, thermal and mechanical shock, and good electrical properties at high humidity.
Weigh the desired amount of #3600 Resin into a clean container and combine with recommended hardener in one of the ratios shown below.
|Hardener||Parts by Weight
per 100 pts. Resin
100 grams @ 25oC
|Hardener||Cure @ 25oC||Cure @ 65oC||Cure @ 100oC||Cure @ 130oC|
|A-110||24 hours||2 hours||---||---|
|A-120||24 hours||2 hours||---||---|
|AB-312||---||6 hours||3 hours||2 hours|