RBC #2360 is a modified, low-viscosity resin offering excellent wettability and air release. It is used both as an adhesive and potting resin. It exhibits high peel strength, excellent shock and vibration resistance. It is ideal for bonding materials with different coefficients of thermal expansion. It bonds well to nickel, aluminum, nylon, polypropylene, glass and wood. As a room temperature potting compound, it offers long pot life, low exotherm, and good thermal and mechanical shock resistance.
Mixed Viscosity @ 25oC,cps: 3,000
Pot Life: 1-2 hours
Shelf Life, (closed Container @ 25oC): 12 Months
Color: Light amber
Specific Gravity @ 25oC: 1.07
Hardness, Shore D: 40
Linear Shrinkage, in./in.: 0.005
Moisture Absorption 10 Days @ 25oC, %: 0.55
Izod Impact Strength, ft. lbs./in. of notch: 11.25
Bond Shear Strength, psi Al/Al @ 25oC: 4,500
Tensile Strength @ 25 deg. C, psi: 3,500
Compressive Strength @ 25oC, psi: 8,000
Thermal Conductivity, cal/sec/cm2/oC/cm X 10-4: 5.20
Thermal Stability, 1000 Hrs. @ 175oC, % Wt. Loss: 1.25
Coefficient of Thermal Expansion, in./in./oC X 10-6: 45.0
Operating Temperature Range, oC: -55 to 100
Volume Resistivity @ 25oC, ohm-cm: 8 x 1012
Dielectric Strength, volts/mil: 430
Dielectric Constant @ 25oC, 100 KC: 3.3
Dissipation Factor @ 25oC, 100 KC: 0.018
The above properties are typical of a semi-flexible formulation cured for 1 hr @ 65oC and 1 hr. @ 120oC.
Weigh the desired amount of #2360 Resin into a clean container and combine with AB-528 Hardener in one of the ratios shown below. Mix thoroughly for a minimum of three minutes by hand, or one minute by machine.
Semi-Flexible, Impact and Shock Resistant: 100 parts RBC #2360, 100 parts Hardener AB-528
Flexible, Excellent Peel Strength: 100 parts RBC #2360, 132 parts Hardener AB-528
Pot life ranges from 1 - 2 hours depending on batch size and hardener ratio. Cure for 24 hours at room temperature (25oC) or 2 hours at 65oC. For optimum properties, cure 1 hour at 65oC followed by 1 hour at 120oC.