RBC #2500 is a thixotropic epoxy adhesive developed for high temperature bonding, offering excellent chemical resistance, and formulated for ease in handling and application. This two-part, solvent-free system cures at room temperature, and when cured at higher temperatures, maintains a non-sag consistency even on vertical surfaces.
Mixed Viscosity @ 25oC,cps: Thixotropic
Shelf Life, (Closed Container @ 25oC): 12 Months
Specific Gravity @ 25oC: 1.18
Hardness, Shore D: 85
Linear Shrinkage, in./in.: 0.011
Moisture Absorption 10 Days @ 25oC, %: 0.20
Izod Impact Strength, ft. lbs./in. of notch: 0.60
Bond Shear Strength, psi AI/AI @ 25oC: 4,850
Tensile Strength @ 25oC, psi: 13,000
Compressive Strength @ 25oC, psi: 19,000
Thermal Conductivity, cal/sec/cm2/oC/cm X 10-4: 5.2
Thermal Stability, 1000 Hrs. @ 175oC, % Wt. Loss: 0.40
Coefficient of Thermal Expansion, in./in./oC X 10-6: 50
Heat Distortion Temperature, oC: 90
Operating Temperature Range, oC: -65 to 155
Volume Resistivity @ 25oC, ohm-cm: 7x1015
Dielectric Strength, volts/mil: 450
Dielectric Constant @ 25oC, 100 KC: 4.3
Dissipation Factor @ 25oC, 100 KC: 0.030
The above properties were determined using Hardener #B-130 cured for 2 hours @ 100oC.
A-110: A rigid, room temperature curing system with limited pot life and fast cure.
A-120: A resilient, low viscosity system with slightly longer pot life, that exhibits excellent resistance to thermal shock.
B-130: A long pot life system with good resistance to heat, chemicals, thermal and mechanical shock, and excellent retention of mechanical properties at elevated temps.
Weigh the desired amount of #2500 Resin into a clean container and combine with recommended hardener in the proper ratio as shown below.
|Hardener||Parts by Weight
per 100 pts. Resin
100 grams @ 25oC
|Hardener||Cure @ 25oC||Cure @ 65oC||Cure @ 100oC|
|A-110||24 Hours||2 Hours||---|
|A-120||24 Hours||2 Hours||---|